Method and structure for buried circuits and devices

ABSTRACT

A method and structure for fabricating an electronic device using an SOI technique that results in formation of a buried oxide layer. The method includes fabricating at least one first component of the electronic device and fabricating at least one second component of the electronic device, wherein the first component and the second component are on opposite sides of the buried oxide layer, thereby causing the buried oxide layer to perform a function within the electronic device. Entire circuits can be designed around this technique.

CROSS-REFERENCE TO RELATED APPLICATONS

This application is a Division of U.S. patent application Ser. No.09/879,530 filed Jun. 12, 2001, the disclosure of which is herebyincorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention involves fabrication of semiconductor devicesusing Silicon-on-Insulator (SOI) technology. More specifically theinvention is directed to the use of the SOI Buried Oxide (BOX) layer asan integral component of electronic devices and circuits.

2. Description of the Related Art

Silicon-On-Insulator (SOI) technology has emerged as an electronicfabrication technique that improves characteristics such as latchup andspeed, although typically at higher manufacturing cost. The term SOItypically describes structures where devices are fabricated insingle-crystal Si layers formed over an insulating film or substrate.

FIGS. 11A and 11B show a typical conventional SOI structure, where athin silicon device layer 110 formed on an insulator 111 is supportedover substrate 112. For current technology the substrate is mostcommonly silicon and the insulator is most commonly silicon dioxide.Devices 113 are formed in device layer 110 and interconnected by surfaceconductors 114. The conventional SOI structure is predominantly createdby one of two techniques.

The first process, known as SIMOX (Separation by IMplanted OXygen),consists of implantation of oxygen into an Si substrate at a prescribeddepth and heating it to form a continuous layer of SiO₂. The SIMOXprocess requires only a single wafer. The alternate process, shown ingreater detail later, is commonly referred to as “Bonded SOI” and startswith two wafers, preferably with at least one having an oxide surface.The first wafer is the carrier wafer which is joined together with thesecond wafer, and the second wafer is “thinned” to leave a layer ofsilicon bonded onto the carrier wafer, separated by an insulator layer.

Both of the techniques have experienced many variations and enhancementsover the years for improvement of yield and lower cost and to achievedesirable device layer quality for uniformity and defects. An importantcharacteristic of conventional SOI that is obvious from FIG. 11B is thatthe insulator layer 111 is used primarily for isolating the silicondevice layer 110 with its active devices 113 from the silicon substrate112. Thus, the conventional wisdom forms devices on the device layer 110on only one side of the insulator layer 111.

The problem with this approach is that, although devices andinterconnects are formed similar to conventional substrates, SOItechniques introduce newer problems such as floating body effects.Additionally, conventional SOI structure takes up considerably more chip“real estate” than required in corresponding non-SOI structure, sincefloating body effects which not an issue with conventional substratesrequire additional connections to the channel regions. There are alsoadded process steps to provide ground interconnections to the substrate.More important, the conventional approach fails to recognize that theinsulator layer could provide more functionality than merely separatingpredetermined groups of devices from the substrate.

SUMMARY OF THE INVENTION

The inventors have recognized that the SOI insulator layer, or BOX(Buried OXide), can be an integral part of a specific device, andfurther, even circuits can be advantageously built around thisinnovative approach. That is to say, the BOX can be considered more thana mere passive isolation mechanism separating layers of devices. It canbecome an integral component even of an entire circuit. As will bedemonstrated, by adopting this innovative approach, a whole newpossibility opens up for SOI technology that provides improved devicedensity and speed and fewer conductor interconnects between devices.

Therefore, an object of the invention is to teach methods in which theSOI insulator (BOX) is used as a building component at the device level.

Another object of the invention is to teach methods in which the BOXserves as a building component at the circuit level.

Another object of the present invention is to teach a method in whichthe BOX is used for functions other than simple isolation between layersof devices.

Another object of the present invention is to teach a method in whichthe BOX is even used for functions other than isolation even within asingle device.

Another object of the present invention is to improve electronic devicedensity on SOI chips.

Another object of the present invention is to reduce the number ofconductor interconnects between devices on SOI chips.

Another object of the present invention is to reduce parasitics andincrease speed on SOI chips.

Another object of the present invention is to teach methods for formingfeatures in the substrate prior to the formation of SOI structure.

Another object of the present invention is to teach methods to formimproved FET devices on SOI.

A still further object of the invention is demonstrate applications thattake advantage of the above methods.

Yet another object of the invention is to demonstrate the above goalsand techniques using established silicon manufacturing processes andequipment.

To achieve the above objects according to a first aspect of theinvention, a method and structure is disclosed of fabricating anelectronic device using an SOI technique resulting in formation of aburied oxide layer. The method includes fabricating at least one firstcomponent of the electronic device and fabricating at least one secondcomponent of the electronic device, where the first component and thesecond component are on opposite sides of the buried oxide layer so thatthe buried oxide layer performs a function within the electronic device.

According to a second aspect of the invention, a method is disclosed offabricating an electronic circuit using an SOI technique, said SOItechnique resulting in formation of at least one buried oxide layer, theelectronic circuit comprising a plurality of interconnected electronicdevices, each electronic device comprising a respective plurality ofcomponents. The method includes fabricating a predetermined first set ofrespective plurality of components to be on a first side of the buriedoxide layer and fabricating a predetermined second set of respectiveplurality of components to be on a second side of the buried oxidelayer, where the second side is the opposite side of the first side, andwhere the buried oxide layer performs a function integral to thefunctioning of at least one of the electronic devices.

According to a third aspect of the invention, a method is disclosed ofSOI fabrication in which a buried oxide layer is formed, where themethod includes forming a first set of device components to be on afirst side of the buried oxide layer and forming a second set of devicecomponents to be on the side opposite the first side, where the buriedoxide layer performs a function integral to the functioning of at leastone device comprised of components from the first set of components andcomponents from the second set of components.

According to a fourth aspect of the invention, a method and structureare disclosed of fabricating a DRAM cell using an SOI technique on asubstrate, where the SOI technique results in formation of at least oneburied oxide layer. The method includes forming a buried capacitorbeneath the buried oxide layer, subsequently forming an FET source anddrain regions on top of the buried oxide layer, and interconnecting thecapacitor to one of the source region or drain region with a viapenetrating the buried oxide layer, where the via is a conductivematerial.

According to a fifth aspect of the invention, a method and structure aredisclosed of fabricating a DRAM cell using an SOI technique, where theSOI technique results in formation of at least one buried oxide (BOX)layer, whereby a capacitor for the DRAM cell is formed by a processincluding forming a buried electrode in a substrate, wherein the buriedelectrode serves as a lower capacitor charge plate and forming adiffusion link between the diffusion region of a transistor located onthe upper side of the BOX and a region to comprise an upper charge plateof the capacitor, where the upper charged plate of the capacitor isformed on the upper side of the BOX when impressing a bias voltage onthe buried electrode.

According to a sixth aspect of the invention, a method and structure aredisclosed of fabricating an electronic circuit having a plurality ofelectronic devices using an SOI technique, the SOI technique resultingin formation of at least one buried oxide layer. The method includesforming an interconnector of conductive material to interconnect atleast two of said plurality of electronic devices, the interconnector atleast partially enclosed by said buried oxide.

According to a seventh aspect of the invention, a method and structureare disclosed of fabricating a dynamic two-phase shift register. Themethod includes forming a buried oxide layer using an SOI technique,forming a plurality of FET transistors to be in a device layer above theburied oxide layer, forming a first clock signal conductor on top of thedevice layer, and forming a second clock signal conductor below thedevice layer, the second clock signal conductor at least partiallyenclosed by the buried layer.

According to an eighth aspect of the invention, a method and structureare disclosed of fabricating a CMOS circuit. The method includes forminga buried oxide layer using an SOI technique and forming a plurality ofFET transistors to be in a device layer above the buried oxide layer,wherein at least two of the FET transistors share a common diffusionregion, thereby electrically interconnecting the two FET transistorswithout using a separate interconnecting conductive material.

According to a ninth aspect of the invention, a method and structure aredisclosed of fabricating a FET using an SOI technique, the SOI techniqueresulting in formation of at least one buried oxide layer. The methodincludes forming a first gate beneath the buried oxide layer and forminga second gate on top of the buried oxide layer.

According to a tenth aspect of the invention, a structure is disclosedof an electronic device including at least one SOI buried oxide layer,where the at least one buried oxide layer performs a function integralto the device.

According to an eleventh aspect of the invention, a structure isdisclosed of an electronic device comprising at least one SOI buriedoxide layer, where the at least one SOI buried oxide layer becomes astructural element integral to the device.

According to a twelfth aspect of the invention, a structure is disclosedof an electronic circuit comprising a plurality of interconnecteddevices, the circuit mounted on a wafer having at least one SOI buriedoxide layer, wherein the at least one SOI buried oxide layer is afunctional element integral to at least one of the devices.

According to a thirteenth aspect of the invention, a structure isdisclosed of an electronic circuit comprising a plurality ofinterconnected devices, the circuit mounted on a wafer having at leastone SOI buried oxide layer, where the at least one SOI buried oxidelayer comprises a structural element integral to at least one of thedevices.

According to a fourteenth aspect of the invention, a structure isdisclosed of an electronic circuit comprising a plurality ofinterconnected devices, the circuit mounted on a wafer having at leastone SOI buried oxide layer, where the two adjacent devices share atleast one device component, thereby electrically interconnecting the twodevices without an interconnecting conductor, and where the SOI buriedoxide layer serves to isolate components of the two interconnecteddevices other than the shared component.

According to a fifteenth aspect of the invention, a method is disclosedof SOI fabrication wherein a buried oxide layer is formed. The methodincludes forming a first set of device components to be on a first sideof the buried oxide layer and forming a second set of device componentsto be on the side opposite, where the buried oxide layer is used for anactive functioning of at least one buried device.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other objects, aspects and advantages will be betterunderstood from the following detailed description of a preferredembodiment of the invention with reference to the drawings, in which:

FIGS. 1A-1C show three exemplary kinds of structure formed in thesupporting silicon body which illustrate how the BOX can beadvantageously used;

FIG. 2 shows exemplary device structures using the techniques taught inthe invention;

FIGS. 2A-2E show exemplary structures formed in the lower sectionsilicon body prior to forming SOI substrate;

FIG. 3A-3E illustrate the bonded SOI process for completing the processof FIG. 2A-2E to form the device illustrated by FIG. 2;

FIGS. 4A-4E show an exemplary set of steps using the SIMOX process for adevice illustrated by FIG. 2;

FIGS. 5A-5D illustrate examples of different device elements formedusing the invention that illustrate advantages of the invention;

FIGS. 6A-6C illustrate an advantage of the invention of using the BOX tointerconnect components without having to use connectors;

FIGS. 7A-7B illustrate another example of the invention, as used toimplement DRAM cells

FIGS. 8A-8C illustrate a second implementation of DRAM cells using theinvention;

FIGS. 9A-9C illustrate an example of the invention for a dynamic twophase shift register circuit, which example demonstrates the BOX as acircuit element;

FIGS. 10A-10B illustrate the invention used for a NOR circuit; and

FIGS. 11 a, 11 b show conventional SOI structures.

Note that the drawings are drawn more to illustrate the inventiveprocesses and structures and are not drawn to scale.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Going back to FIGS. 11A-11B illustrating the conventional SOI device,wherein oxide layer 111 separates device layer 110 from substrate 112.FET devices 113 are built into device layer 110. One conventionaltechnique forms FET transistors with the following steps: a gate oxideis formed by a surface oxidation of layer 110, a gate electrode isformed by deposition and patterning of polysilicon, and source and drainregions are formed by implantation of a dopant. These source/drainregions, gate electrodes can then be surface wired 114 by commoninterconnection processes.

Turning now to the invention, FIGS. 1A-1C illustrate respectively aburied gate 13, a buried wire 14, and a buried capacitor 15 which areexemplary structures resulting from the present invention to use the BOX12 as an integral part of devices and even entire circuits. Either theSIMOX technique or the bonded technique can be used. Substrate 10receives device components which are then complemented with components16 in the device layer 11 above BOX 12. Similar to conventional SOIstructures of FIGS. 11A-11B, surface conductors 17 could still be usedto interconnect devices if desired, although the invention permitsinterconnections in a different manner. Details of forming thesestructures and the advantages of the invention will become obvious toone skilled in the art after an understanding of the following sections

FIG. 2 shows an exemplary SOI structure 20 in which two FETs 20A, 20Bare constructed with the BOX 24 as an integral part at the device level.Buried elements 21,22 have been formed in the lower section 23. In thisdiscussion element 21 is a body contact and element 22 is a buried gate.BOX 24 separates lower section 23 from upper section 25 containingadditional source and drain regions 26, 27.

FIGS. 2A through 3D show an exemplary formation using the bonded SOItechniques to result in the structure 20 shown in FIG. 2. An exemplaryformation using SIMOX is illustrated in FIGS. 4A-4E. The buried elements13, 14, 15 shown in FIGS. 1A-1C demonstrate that the buried elements 21,22 in FIG. 2 could be variously a gate, capacitor, or wire, depending onthe process/material used in forming the elements. Therefore, it shouldbe obvious that a great variety of devices can be constructed using theconcepts taught by this invention.

Concerning the bonded technique, FIG. 2A shows a method of constructinglower section 23 whereby a silicon dioxide layer 200 having thickness of250-2500 A is formed on a silicon carrier substrate 201. This layer 200and its thickness is not critical since it is used as a selective maskin etching trenches 202. It is quite likely that the insulator etch andlater on polysilicon polish process will remove some of the oxide layer.In a preferred process, the BOX layer will be reformed after removingany residual mask layer at the same step as forming trench sidewallinsulator. If needed, a silicon nitride layer 203 (not shown) ofthickness in the range of 500-2500 A is used in addition to silicondioxide 200. Silicon nitride, although not intended as part of the BOXlayer, can provide good selectivity for etching and chemical mechanicalpolishing and will protect the underlying oxide or the substrate. Whennitride is used on top of an oxide layer, any remaining nitride layerafter completion of buried structures in substrate 23 will be removedprior to bonding it to the device wafer. The final insulator stack forthe mask layer preferably comprises oxide/nitride/oxide layers, althoughnot all layers are essential. The thicknesses of the insulators arechosen depending on the depth of the trench 202 which in turn dependsupon the specific component to be placed in the trench, but typicallythe combined thickness of the insulator stack is less than 5000 A. Forforming a buried gate 13 (see FIG. 1A), the trench depth 204 istypically about 2000-5000 A, similar to the typical thickness of gateelectrodes. For forming a buried wiring layer 14 (FIG. 1B), the depth ofthe trench is typically in the range of 5000 Angstroms to 2 micron. Forforming a trench capacitor 15 (FIG. 1C), a larger depth of the order of2-6 microns is chosen.

The process of etching vertical trenches in silicon substrate is wellknown. For example, for the exemplary buried gate process a standardlithography can be used to create the pattern in a resist mask, followedby a directional etching using a Cl₂/Ar plasma such as described in U.S.Pat. No. 4,139,442, assigned to the assignee and incorporated herein byreference. Other commercially available etch processes are alsosatisfactory for the trench etch. After removing the resist mask, thesubstrate is similar to that shown in FIG. 2B.

Subsequently, as shown in FIG. 2C, to further develop the buried gatestructure, an insulation layer 205, 206 will be incorporated on thesides/bottom of the trenches 202. This insulator layer 205, 206typically would be an oxide or nitride layer or a combination thereofand is formed by depostion, insitu conversion of silicon, or acombination of processes. If themal oxidation is chosen, it can useconventional steam or dry oxygen in a furnace, a rapid thermal heatingin an oxidizing ambient, or any equivalent methods. Deposited oxidesproviding good conformality can also be used. For buried gates or buriedwires, it is desired to have these conductors (yet to be formed) fullyencased on the sides and bottom 207 with insulator. For otherapplications such as body contacts, the insulator in the bottom of thetrench is not desirable 208, and for removing the bottom insulatorsection, a directional etching using fluorine-containing gases such CF₄or SF₆ can be used in a directional mode to selectively etch the newlyformed insulator (oxide) 205 from the horizontal bottom surface 208,leaving only the insulator along the trench vertical side walls.

FIG. 2D shows that the trenches are then overfilled and planarized backto result in a selected conductor 209, 210 embedded in the trench. Theconductor 210 can be selected from polysilicon, tungsten or molybdenumand alike for close thermal matching with silicon and stability at thefollow-on high process temperatures. An epitaxial Si 209 process canalso be used. In one preferred process polysilicon 210 is formed bydepositing in an LPCVD reactor at about 600-700 C, using dichlorosilaneand a dopant precursor such as phosphine.

The width of the gate pattern for the buried gates is restricted by thespecific design ground rule. The polysilicon conductor 210 whendeposited typically will fill and provide approximately a planar topsurface. The polysilicon is then preferably chem-mech polished using,for example CABOT SC-I, a colloidal silica in an aqueous KOH solutionwith pH i10. Other polishing slurries commercially available and knownin the field for polishing polysilicon with good selectivity to siliconnitride or silicon dioxide can also be used.

At the end of polishing, the polysilicon 210 in the trench may beslightly recessed with respect to the insulator 206 but has a highdegree of smoothness, typically a few nanometers. Specifically, thepolishing process described in the publication “Characterization ofPolysilicon Oxides Thermally Grown and Deposited on the PolishedPolysilicon Films”, by Tan Fu Lei et al., IEEE Transactions on ElectronDevices, vol. 45, No.4, April 1998, pages 912-917 is extremelyattractive for producing a highly smooth polysilicon surface. The polishstop layer silicon nitride 203, if it was used, is now removed from thetop horizontal surfaces by wet etching selective to silicon and silicondioxide, as is well known in the art.

FIG. 2D represents approximately the appearance in cross section of thesubstrate after the polishing, with thermal oxide 200 on the tophorizontal surfaces and polysilicon 210. All surfaces are then subjectedto post CMP clean using a dilute 50:1 ammonia in a megasonic cleaner. Anadditional RCA clean process could be used. At this point the heightdifferences between the polysilicon and the silicon substrate istypically less than 500 A Next, as shown in FIG. 2E, an oxide layer 211of about 500-1000 A is formed over the polysilicon and remnants ofthermal oxide layer 200. When 211 is formed by thermal oxidation, thethickness of oxide over doped polysilicon is expected to be somewhatthicker than the oxide growth in the surrounding Si areas. If thermaloxidation is used, 1000 A of oxide will consume about 400 A ofpolysilicon, whereas a slightly thinner oxide layer is formed over thesilicon. The surface of the oxide is chem-mech polished using a stiffpad and suitable oxide slurry such as Cabot SC-1 so as to form acontinuous and smooth oxide layer. If needed, other thinning processessuch as etching can be used to compliment the polishing to achieve thedesired oxide thickness over the polysilicon gate electrode. The processis typically designed to leave about 100-250 A of silicon dioxide 211over the polysilicon gate.

Alternatively, a high quality CVD silicon dioxide of about 200-1000 A isdeposited and polished back to leave a desired thinner oxide layer overthe polysilicon gate region. Because of the method described above forthe formation of the polysilicon in the trenches, the resultingstructure shown in 2E will have a thinner oxide over the polysilicongate region 212 and a thicker oxide 213 over the silicon substrateregions.

As a possible alternative, if CVD tungsten is used as the buried gateelectrode. Instead of depositing polysilicon, a seed layer of TiN orTi/TiN or TiW is deposited and followed by CVD W deposition using wellestablished techniques with silane, hydrogen and WF₆ gases in a thermalreactor. The blanket metal film will appear similar to the polysiliconplanar structure after deposition, which can be Chem-mech or plasmaetched back to remove the W and the seed layers from the top surfaces.In one preferred process, the W layer will be recessed by using a plasmaetch followed by forming a cap of silicide or silicon. The purpose offorming a tungsten silicide or polysilicon cap is again to form a thinoxide surface over the electrode. If a buried body contact is beingformed, then there is no need to form the additional oxide on thesurface of the encased conductor. Any oxide formed on the encasedconductor is selectively removed. Other known variations of processescan be used to achieve essentially the structure shown in FIG. 2E with avariety of materials to form the components.

Continuing with the bonded technique, FIG. 3A shows the development ofthe upper section 25. Substrate 30 is prepared to become a temporarycarrier. First, as an optional but one preferred technique to facilitatethe removal of excess wafer material after the lower section 23 andupper section 25 have been joined (reference FIG. 2), hydrogen isimplanted 31 into the silicon substrate 30. Epitaxial layers 32 ofsilicon with different dopants from substrate or silicon-germanium maybe deposited over the silicon substrate. Optionally, in the absense of adeposited epitaxial layer, the top surface region of the devicesusbtrate will become the device layer. The “Smart-Cut” processutilizing the epitaxially deposited layer is described in greater detailin U.S. Pat. No. 5,882,987, hereby incorporated by reference. Theprocess of hydrogen implantation forms a silicon hydride layer 31 onsuitable annealing, that becomes the basis of the Smart-Cut technique toallow separation of the unwanted layers of carrier wafer 30 after thetop section 25 is bonded to the bottom section 23. Although Smart-Cut isthe exemplary process for transferring the device layer 32, alternateprocesses of combining etching and polishing, such as those described inU.S. Pat. Nos. 4,601,779 and 4,735,679, can also be used.

Device layer 32 is deposited epitaxially using, for example, SiGe, butthe specific material depends upon the device to be fabricated. An etchstop layer is optionally added on top of the device layer, which couldbe simply a highly doped silicon layer or a silicon-germanium layer, asper the teaching of the above mentioned U.S. Pat. No. '987. A thinthermal oxide 33 of thickness 50-200 A is optionally grown on themonocrystalline surface. When the end device will include body contact,a bare silicon without oxide layer 33 is used. Hydrogen 31 is implantedunder conditions taught in '987, preferably at a depth below thedeposited device layer. As shown in FIGS. 3B and 3C, the device wafer 25is then flipped and attached to the carrier substrate 23 prepared inFIGS. 2A-2E. By way of exemplary technique, the oxide surfaces arejoined using surface treatments to make oxide surfaces 33,211hydrophilic. Such attached wafers have sufficient bonding to withstandmost handling. The wafers are now heated at about 300-600 C to completethe Smart-Cut process as shown in FIG. 3D, in which the excess wafersection 34 is then removed. In one variation of the Smart-Cut process,the wafer is heated to a temperature range 250-400 C to segregatehydrogen to the device layer interface (in the case of SiGe depositedlayer), followed by cleaving the substrate 34 along the hydrogenimplanted surface using water jets.

The transferred device layer surface 35 is now finished to a smoothsurface by polishing or etching or along the teaching of U.S. Pat. No.'987 using an optional etch-stop layer Thus, an SOI wafer 20 (see alsoFIG. 2) with buried body contact 21 and buried gate electrode 22 has nowbeen formed. The gate oxide 36 on the buried gate electrode is roughlyequal to the thickness of oxide 33 or to the sum of the two surfaceoxides 33, 211, and can be between 100-500 A, depending upon theselection of thickness of individual oxide layers. As discussed earlier,one of the oxide layers 33 can also be conveniently not formed sincebare Si surface can also be effectively bonded to silicon dioxide. Asdiscussed in the IEEE publication mentioned above, the polyoxide formedover polished polysilicon, either thermally formed or deposited, is veryhigh quality, approaching that required for gate oxide applications.

Referring now back to FIG. 2 showing the completed SOI structure, topgate electrodes 214, 215 are formed on top of a gate oxide layer 216. Toachieve this, typically a polysilicon layer deposited on top of the topgate insulator is patterned to create top gate electrodes 214, 215. Thedevice layer 25 is now the channel or body layer for both the top gates214, 215 and bottom gate structures 21,22. The top gate electrodes 214,215 could be a polycide layer if the application would require a lowerresistance.

FIGS. 4A-4E illustrate an alternate formation using the SIMOX process ofa corresponding buried contact and buried gate electrode structure. Theprocess steps to create the buried structures 209, 210 is same as usedin FIGS. 2A-2D. Thus, FIG. 4A starts as being the same structure shownin FIG. 2D with trench/sidewall/conductor 209 andtrench/sidewall/bottom/conductor 210 structures filled with dopedpolysilicon or other suitable refractory conductor material. Polysiliconwill arbitrarily be assumed here as the conductor. FIG. 4B shows surfaceinsulator 200 having been removed and gate insulator 401 havingthickness of 50-200 angstroms being formed over the electrode 210 to beused a buried gate. In a preferred process, this gate insulator 401 isformed by oxidizing the polysilicon with the oxide insulator 200 stillin place and then the insulator 200 is removed by a polish or etchprocess. In one preferred embodiment of this polysilicon oxidationprocess, the insulator 200 has an additional SiN layer to allow only thepolysilicon to be exposed and thereby oxidized in a controlled manner.

Thereafter, oxide layer 200 is removed and any insulating layer 402 overthe buried contact 209 is selectively removed by means of a block-outmask (FIG. 4B). A device layer 403 is deposited under epitaxialcondition, which forms a single crystal over the all silicon surface(FIG. 4C), except that small regions of polycrystalline Si 404, 405 areformed over polysilicon and oxide surfaces. The regions 404 and 405 canbe formed single crystalline if epitaxial conditions for lateral growthcan be used, such as taught in U.S. Pat. No. 5,646,958, the contents ofwhich are incorporated herein by reference. In FIG. 4D an implantationmask 406 is formed over the buried regions and oxygen ions 407 areimplanted into substrate 201, using typical SIMOX conditions such astaught in U.S. Pat. No. 6,043,166, the contents of which areincorporated herein by reference.

The energetics of the implantation controls the depth of the implantedions 407. For a buried gate 210 or body contact 209, the implant depthis chosen to be slightly beneath the device layer. For buried wires andcapacitors, since the structures are fully encased in insulator, thisimplantation location is less critical but preferably the implant depthis chosen to be near the device layer and substrate interface so that atleast part of the BOX layer formed can cover the top of the wire andcapacitor elements.

Using anneal conditions and timing such as taught in U.S. Pat. No.6,043,166, the implanted oxygen is converted into a buried oxide layer408 as shown in FIG. 4E. Transistors are formed with gate oxide 409 andgate electrodes 410 using standard masking and deposition techniques toresult in the structure similar to that shown in FIG. 2.

Even though the SIMOX process has been described using a set ofpreferred process steps with a view to forming buried gate electrode andburied body contact elements, it should be obvious to one skilled in theart, the above described process steps can be used as well to form otherelements such as buried wiring layer or capacitor elements by smallvariations to the above process.

FIGS. 5A-5D show a magnified view of three exemplary SOI structures,buried gate electrode 50A (FIG. 5A), body contact 50C (FIG. 5C),andburied wire 50D (5D), for purpose of demonstrating additional advantagesof the invention.

FIG. 5A shows the resultant structure 50A when the lower section 53 andupper section 54 are formed so as to result in a buried gate electrode58A. Of particular interest in this structure 50A, and which differsfrom the prior art, is that the buried oxide (BOX) layer 55A is now anintegral part of the second gate device 58A. Specifically, the SOIburied oxide layer 55A acts as the second gate insulator for the buriedFET and also as isolation of the device layer 54 from the substrate 53.

Also of interest in the FIG. 5A structure 50A is that the buried oxidelayer 55A forming the second gate insulator will generally be adifferent thickness than the upper oxide layer 59 forming the upper gateinsulator structure. This different thickness can be a useful techniquefor controlling the dual gated device characteristics.

FIG. 5B shows an example of a top view of the dual gates layout. Theeffective shapes 501, 502 of the two gates 56 and 58A can have differentlength, width or shapes to facilitate easier contact to respective gatesor to obtain a device of different channel lengths so that a dual gateand single gate channel regions can be combined in parallel to achievedifferent gains. The top and bottom gates 56, 58A can be positioned tosmall variations such as different angles (bent gates) to facilitate forexample, better lay out of wiring tracks on the top or easier contact tobottom.

FIGS. 5A and 5B also show the technique of connecting the upper andlower gates 501, 502 by vias 503, 504 so that when the gate voltage isimpressed on the top, it acts on both top and bottom, improving thedevice performance. In the inventive process, this connection can beachieved using a simple process of using two layers of polysilicon forthe top gate electrode, such as described in U.S. Pat. No. 4,341,009,which is incorporated herein by reference. Using this referencedprocess, formation of the via 503 and 504 is straightforward. '009describes a process using dual polysilicon to form buried contacts.First a thin layer of polysilicon or polycide is deposited on the gateoxide, followed by etching a contact hole through the thin electrode,gate oxide and body channel layer, and buried gate oxide to the buriedgate electrode. A second gate electrode layer is now deposited andpatterned to make the first and second electrode contact. During thisprocess, it is also possible to make other connections such as bodycontact, as additional contact can be made to the carrier substrate.This technique is used here where the gate electrode is formed in twosteps. In step 1, a first polysilicon layer is blanket deposited overthe gate oxide in forming the top device, followed by etching the via. Asecond polysilicon layer now is deposited on the first polysilicon whichmakes the contact to the body layer or bottom electrode while providingadditional thickness to the top gate electrode. This stack is nowpatterned to include top gate electrode and the via connection. A moretradional process step can be used whereby the top electrode is formed,via 403 or 404 is etched in a separate step and a local interconnect ora contact stud metallization used to connect the top and bottomelectrodes.

In SOI devices, there is a strong need to connect the body siliconregion to a common ground or substrate potential to stabilize thethreshold voltage. FIG. 5C shows one such structure 50C having devicelayer 54, BOX layer 55C, and substrate 53. Region 58C which is apolysilicon electrode that contacts directly the device layer 54 at thebody region of the gate 56. Forming such a polysilicon electrode hasbeen discussed already relative to FIGS. 2-4. This preferred embodimentprovides a required body contact with no additional space needs, withoutany need for additional photo process, layer depositions, etc. Thisembodiment therefore represents an attractive process for forming an SOIburied contact.

FIG. 5D shows a buried wire 52, which can be used for making localinterconnect between a contact of a transistor to an adjacent transistoror to a resistor or capacitor. For schematic simplicity one via contactis shown extending a via from a buried wire to the top surface above thedevice layer. In typical applications multiple vias are provided fromthe same buried wire which can be used to connect devices at the topsurface. Since the buried wire layer 52 is at a different plane than thedevices, wirability is easily achieved, wihtout concenrning of crossingover other devices or other connections on the top surface.

One of the important features of this invention is the ability to usethe SOI buried layer to form separate devices while still retaining acommonality between the devices. This feature allows devices to beinterconnected without having to provide interconnection conductors,thereby improving device density. This feature is exemplarilyillustrated in FIG. 6A and FIG. 6B for the case of forming separate FETs61, 62 sharing a common body layer 64. Additional specific examples willbe discussed later and many more should be obvious to one of ordinaryskill in the art, but the examples in FIGS. 6A, 6B will demonstrate theimportant concept that entire circuits can be more effectivelyfabricated by considering the BOX as an important component at not onlythe device level but also at the circuit level, as will be discussed inmore detail shortly.

In FIG. 6A is shown the general case of two devices 61 and 62 isolatedby SOI buried layer 63 and sharing a common body layer 64. This featureenables formation of many more FETs, with each layer of FET design beingoptimized by separate layout restraints. As discussed earlier, buriedelectrodes and body contacts can be advantageously used to interconnectthese devices to form circuits. When the buried gate 62 is laterallyseparated from the top gate, the source/drain regions for the buriedgate can be formed by patterning dummy gates over the buried gate as amasking layer and implanting selective regions to complete the buriedFET device.

For many applications, the source/drain of adjacent devices can beadvantageously shared, as shown in FIG. 6B, to provide specific circuitinterconnections. This technique increases the density of device layoutsince this configuration becomes a series connection at node 68 betweenFETs 65, 66 without having to use additional interconnectors. It shouldbe obvious that parallel connections are similarly possible.

FIG. 6C illustrates the degree of freedom in the layout of the topelectrodes 61,66 and bottom electrodes 62,65 resulting from thisinvention. For example, one or both of the gates can have bends in orderto meet other requirements or provide other advantges such as ease ofwirability.

FIG. 7A illustrates a schematic of a conventional DRAM cell using asingle FET 75 and a single capacitor 70. One electrode of the capacitoris connected to the drain region of the FET 75 and the other electrodeis grounded. FIG. 7B shows the SOI device embodying two of these DRAMcells and taking advantage of the invention, the first using a top gateFET 75A and the second a buried gate FET 75B. Buried capacitors 70A, 70Bare formed in the substrate 78 and top gate for 75A and buried gate for75B are connected to the capacitors using vias 74A, 74B. The structureof FIG. 7 b is formed by the combination of substrate 78 with a devicelayer 77 through an intermediate BOX layer 79. Various possibleprocesses that can be used to form these structures have been describedalready with the aid of FIGS. 2-4.

The formation of capacitors 70A, 70B in a substrate, for example, hasbeen specifically discussed with the aid of FIGS. 2A-2D. The buriedconductor 73A, 73B with the right choice of trench dimensions andcapacitor node dielectric 71A, 71B (oxide or oxide/nitride formed on thetrench walls) will determine the capacitance value of the buriedcapacitors. The capacitor ground electrodes can be formed either by useof a highly doped substrate 78, or by diffusion drive-in of dopants toform a a highly doped external regions 72A, 72B in the substrate alongthe perimeter of the capacitors 70A, 70B prior to forming the nodeinsulator. This step and additional process steps for forming such astructure is known and described in U.S. Pat. No. 5,770,484, whichcontents are herein incorporated.

In contrast to processes where the buried capacitor is formed subsequentto the SOI substrate, the process described here, where the buriedcapacitor was formed prior to the SOI structure, offers processsimplicity in comparison with other SOI trench capacitor processes andcan provide better yields and lower cost.

FIGS. 8A-8C show a variation of the DRAM cells discussed in FIGS. 7A-7B.FIG. 8A is a well known prior art schematic diagram of a single devicestorage capacitor circuit which uses a single transistor Q1 and astorage capacitor C1. Use of depletion capacitors are well known in theart (see for example U.S. Pat. Nos. 4,163,243 and 4,259,729). The gateof Q1 is activated by a high voltage to turn Q1 on, thus allowing thedata signal level on bit-line BL0 to be transferred to the capacitor C1.The schematic shown in FIG. 8A is similar to the schematic in FIG. 7A,except that the capacitor node labeled VDD was at ground potential. FIG.8B illustrates one embodiment of using a single depleted capacitor 80utilizing a positive bias voltage impressed on the buried electrode tocreate an accumulation region 81 (counter electrode) in the device layer82. An important novelty of this circuit application is in the physicalarrangement of the transistor Q1 (83) located on the top of the commonshared semiconductor region 82 and the capacitor C1 (80) located on thebottom side of that same shared region. This structure is made possibleby the semiconductor teaching of this invention. FIG. 8B will be furtherdescribed in the following paragraph but it should be explained that amultiple variations on this scheme are easily visualized.

In the embodiment of FIG. 8B the data bit to be stored is presented tothe cell on bit line BL0. Transistor 83 (Q1) is activated, as previouslystated, by a high signal applied to its gate 84, thus allowing thevoltage level of BL0 to be transferred to capacitor 80 (C1). As is wellknown in the art, the DRAM cell is read out by preconditioning BL0 to apredetermined voltage level that is between a logical 1 high and alogical 0 low voltage level. Bit line BL0 is connected to a senseamplifier (not shown) which will differentially sense the voltagebetween BL0 and a reference voltage. A high voltage is applied to WL1the gate of transistor Q1 . This turns Q1 on and the signal stored oncapacitor C1 will be transferred to BL0. This signal will be very smallcompared to the signal that was originally written into the cell usingBL0. The sense bit line BL0 will be disturbed electrically in either thepositive voltage direction or negative voltage direction from itspredetermined intermediate level depending on the state stored incapacitor C1. The sense amplifier attached to BL0 will sense and amplifythis small voltage disturbance.

FIG. 8B shows that one side of capacitor C1 is connected via a diffusion85 to transistor Q1. The other electrode of C1 is a plate formed withpolysilicon electrode of capacitor 80. The insulator 86 overlying theelectrode of capacitor 80 (C1) is the capacitor dielectric. Thisdielectic could be the same or similar material SiO₂ as in BOX layer 87.It could also be a different material such as a high dielectric materialallowing a larger value of capacitance for C1 using the same plate areaas this material can be formed during the formation of the buriedcapacitor electrode by deposition.

The arrangement of electrodes of capacitor becomes clear by comparingFIG. 8A and 8B. The diffusion region 85 connects the top electrode ofthe capacitor C1, to a plate-like region formed by inducing charge onthe top surface of the thin dielectric 86 (oxide or high dielectricmaterial) by applying a positive potential to the lower plate of C1. Thepositive potential causes negative carriers to be attracted to the topside of C1 making it conductive and forming the top plate The bottomplate of the capacitor is simply the buried electrode of capacitor 80.

One aspect of novelty in this structure is the location of C1horizontally relative to Q1. C1 may be located substantially under Q1which produces a minimum total cell area, allowing maximum DRAM memorydensity on a unit area of silicon wafer. It may, however, be locatedsubstantially outside the region covered by the gate of Q1 for a minimumdensity result and still operate. The point is that the location of C1relative to Q1 is non critical, so long as C1 does not come closer tobit line BL0 than some minimum dimension established by a leakagecurrent/storage cell retention time criteria.

FIG. 8C is an extension of FIG. 8B, wherein the capacitor is provided byforming the structures 80B and 80T, where 80T is now formed on top ofthe device layer 82. The advantage of this is that the area of capacitor80 can be cut in half allowing for greater overall packing density. Inaddition to using high dielectric constant insulators for thecapacitors, one can also use roughened surface electrodes to increasethe capacitor electrode area. Both these techniques are well known inthe art. Additional variations of structure and materials are possiblewithin the general concepts of forming buried structures taught in here.

FIGS. 9A-9C illustrate an application of building and operation of adynamic two phase shift register using the invented structure. FIG. 9Ashows a conceptual vertical structure utilizing the semiconductorprocessing teaching of this invention to construct four N-typetransistors that is connected as per the Figure C schematic to provide atwo phase dynamic shift register with the FIG. 9B timing diagram. Thesedynamic shift registers have been a classical circuit technique to storedata.

FIG. 9A shows the cross section of one possible SOI structure created bya substrate 91, a device layer 92, and an oxide layer 90 separating thetwo. Further, along the teachings of this invention, two buried gatetransistors 941 and 943 are formed in the substrate region 91. Two topsurface FETs 942, 944 are formed using additional process steps on thedevice layer. All the FETs are N-type, as determined by the choice ofdopants in the device layer and Source/Drain regions, and all sharingthe same body layer 92. By use of overlapping source and drain regions95 between adjacent FETs, the series connection of the transistors as inFIG. 9C is achieved without a need for any external wiring.

In a two phase dynamic shift register two transistors are used to storeone bit of data. In the case of FIG. 9C, transistor 941 and 942 togetherstore bit 1 and transistors 943 and 944 store bit 2. Referring to FIG.9B, clock C1 signal 96 is applied to the gate of transistors 941, 943,and clock C2 signal 97 is applied to wire connected to gates oftransistors 942, 944. The data bit is actually stored on the parasiticcapacitance of the circuit, such as the diffusion capacitance. Two clocksignals 96, 97 are used to control the shifting of the data from one bitlocation to the next. One bit is shifted one position by applying clocksignal C1 (a high) followed by clock signal C2 (a high). The clocks arenon-overlapping meaning that C1 and C2 are never both high at the sametime. Eventually the data entered into the shift register is attenuatedand lost after some number of shift positions unless it is restored inamplitude by a gain stage. Variations of the two phase shift registerscan be constructed with more transistors than shown in FIG. 9A so as torestore or amplify the data at each bit position in the serial string.The circuits for shift registering and amplification are known in theart and the novel aspect of the present invention is the two phase shiftregister structure shown in FIG. 9A, which provide space saving andgreater density.

The two phase shift register structure of this invention register isbased upon the very important semiconductor processing teaching of thisinvention that allows transistors to be isolated by BOX layer 90 to beformed on top and in bottom of a shared region 92 of semiconductingmaterial.

In the structure shown in FIG. 9A the transistors do not lie one aboveanother but are staggered such that the source of one transistor isshared with the drain of a second transistor, an embodiment earlierdiscussed with FIG. 6B. As can be readily seen, one of the novelties inFIG. 9A is that the two transistors of this invention 941 and 942,unlike prior art, do not reside on the same vertical level, typicallyboth on top. In this invention, one of the transistor 941 (Q1) is in thebottom, and the next transistor 942 (Q2) is on the top. The wiring ofthe clock signal C1 to the gate of Q1 takes place below the common layer92 structure, at least in part, where it is necessary to connect to gateregion, i.e., via polysilicon. Similarly, the corresponding wiring to Q2takes place above the common layer 92 structure providing a means toconnect clock signal C2 to the gate region of transistor Q2. In thismanner the necessary wiring to gates on either the top side or thebottom side is substantially reduced in utilization of availablereal-estate on any one side.

Further, if geometries of the transistors, diffusions, and gate wiringwere such that a conflict for available real-estate existed whenattempting to wire the gate regions of two sequential transistors in theshift register chain, such conflict would be substantially reduced oreliminated by constructing the shift register in an alternating fashionof top/bottom transistor location as shown in FIG. 9A. The circuitchosen to demonstrate this concept is the two phase dynamic shiftregister because it is a well known application of classical MOSFETfunction. However other circuit applications would obviously benefitequally well with reduced gate wireability congestion thus allowing forimproved device/circuit density.

FIG. 10A and 10B show the application of the subject disclosure to aCMOS NOR logic circuit. The FIG. 10A schematic shows a two-way logicalNOR circuit. Input signals A & B are connected to the gates oftransistors Q2 & Q4 and Q1 & Q3, respectively. Transistors Q1 and Q2 areP-type transistors and transistors Q3 and Q4 are N-type. This schematicis well known and one of the most widely used logic circuits. The otherwidely used CMOS circuits are the NAND and the simple inverter circuit,and the implementation of the invention into these well known circuitswould be obvious to one of ordinary skill in the art.

The structure of the NOR circuit in FIG. 10B represents a verticalcross-section of a semiconductor chip utilizing the subject invention. Asubstrate 101 and a device layer 103 are separated by a BOX layer 102.The transistor Q4 is formed within the substrate (buried) using theprocess steps taught in the preferred embodiments. The transistors Q1,Q2 and Q3 are formed on the device layer using conventional processes ofoxidation, gate electrode deposition, patterning etc. The scale of thesemiconductor geometry is simplified here to assist the understanding ofhow the NOR circuit of FIG. 10A is realized. The most dramatic benefitand novel benefit apparent in FIG. 10B is seen in the location oftransistor Q3 directly above transistor Q4. It should be noted thattransistors Q1 and Q2 are constructed on the same horizontal axis. Sincethe transistors Q1, Q2 are P-type and Q3 and Q4 are N-type, the devicelayer has isolation regions to separate the different dopants in thedevice layer corresponding N-type and P-type regions. The currentindustry practice is to have the placement or physical location of alltransistors on the same horizontal plane.

However, this invention allows a unique means to fabricate transistorQ3, Q4, one above the other, thus allowing for a significant reductionin chip size for a given logical function. It should be noted that thisis the technique discussed earlier in which components are connected inparallel without requiring separate interconnection conductors.

Additional benefit will be apparent in this structure in the arearequired for the commonly shared source drain diffusions shared bytransistors Q3, Q4. In particular the area of the common drain diffusionof Q3 and Q4 shared with the source diffusion of Q2 is reduced in areasuch that the switching time on the NOR circuit is significantlyreduced. This common node or diffusion also serves as the output node ofthe circuit. Since any capacitance reduction results in a reducedcircuit delay (switching time), the speed is additionally increased. Theconcept here is shown for a NOR circuit but is also readily applied tothe popular NAND logic circuit and many other circuit types found in thecurrent CMOS logic technology industry that produces today'smicroprocessor chips and ASIC custom chips.

These are but some examples of circuits that can be formed utilizingburied devices in conjunction with traditional FETs and other devices.Many ASIC applications can benefit with the additional design groundrules allowed by the inventive devices being available in the buriedsubstrate.

The examples discussed also demonstrate that with these techniques theburied oxide can be used for more than simple isolation. The BOX hasbeen shown to be available for other functions such as the gate oxidefor a buried transistor and the pass-through for a body contact.

While the invention has been described in terms of preferredembodiments, those skilled in the art will recognize that the inventioncan be practiced with modification within the spirit and scope of theappended claims.

1. An electronic device provided on a semiconductor-on-insulator (SOI)substrate, comprising: at least one first transistor having a gateelectrode disposed above a buried oxide layer of the SOI substrate; andat least one second transistor having a gate electrode disposed belowthe buried oxide layer, wherein the buried oxide layer includes at leastone thin region and at least one thick region, the thin region adaptedto perform a function integral to the electronic device.
 2. Theelectronic device of claim 1, wherein the thin region is selected tofunction as the gate dielectric insulator for the second transistor. 3.The electronic device of claim 1, wherein the first transistor and thesecond transistor are field effect transistors (FETs) having source,drain and channel regions provided in a common device layer.
 4. Anelectronic circuit provided in a semiconductor-on-insulator (SOI)substrate, comprising: a plurality of interconnected field effecttransistors (FETs) having elements disposed in a device layer overlyinga buried oxide layer of the SOI substrate, wherein at least one of theinterconnected FETs includes a portion of the buried oxide layer as afunctional element integral to its operation.
 5. The electronic circuitof claim 4, wherein the portion of the buried oxide layer is adapted tofunction as a gate dielectric of the at least one FET.
 6. The electroniccircuit of claim 4, wherein at least one of the interconnected FETsincludes an element disposed beneath the buried oxide layer.
 7. Anelectronic circuit comprising a plurality of interconnected field effecttransistors (FETs), the FETs provided on a semiconductor-on-insulator(SOI) wafer having a buried oxide layer, the FETs including a first FEThaving a gate electrode disposed on a lower side of the buried oxidelayer, and a second FET adjacent to the first FET, having a gateelectrode disposed on an upper side of the buried oxide layer oppositethe lower side, the first and second FETs sharing a device layer,whereby the first and second FETs are electrically interconnectedwithout an interconnecting conductor.
 8. A two-phase shift registercircuit, comprising: a first FET and a second FET connected in series,the first FET having a gate adapted to receive a first clock signal; thesecond FET having a gate adapted to receive a second, non-overlappingclock signal; at least one of a source and drain of the first FETcoupled to receive an input data signal; and at least one of a sourceand drain of the second FET coupled to output an output data signal,wherein the first and second FETs are operable to shift the input datasignal to the output data signal in accordance with the first and secondclock signals.
 9. The two-phase shift register circuit of claim 8,provided on an SOI substrate having a buried oxide layer and a devicelayer.
 10. The two-phase shift register of claim 9, wherein gateelectrodes of the first and second FETs are disposed on opposite sidesof the buried oxide layer.
 11. A complementary metal oxide semiconductor(CMOS) NOR circuit provided on a semiconductor-on-insulator (SOI)substrate having a buried oxide layer and a device layer disposed abovethe buried oxide layer, comprising: a first p-type field effecttransistor (PFET) and a second PFET connected in series, the first andsecond PFETs each having a source terminal, a drain terminal and a gateterminal, wherein the source terminal of the first PFET is coupled toreceive a supply voltage; a first n-type field effect transistor (NFET)and a second NFET connected in parallel, the first and second NFETshaving a common drain terminal and a common source terminal, wherein thecommon source terminal of the first and second NFETs is coupled forproviding a connection to ground, wherein the drain terminal of thesecond PFET is connected to the common drain terminal of the first andsecond NFETs, and the gate electrodes of the first and second NFETs aredisposed on opposite sides of the buried oxide layer.
 12. The circuit ofclaim 11, wherein the gate electrodes of the first PFET and the secondNFET are coupled to receive a first input signal, the gate electrodes ofthe second PFET and the first NFET are coupled to receive a second inputsignal, and the common drain terminal of the first and second NFETs iscoupled to provide a NOR function output in accordance with the firstand second FETs.
 13. The circuit of claim 11, wherein the first andsecond PFETs are both disposed above the buried oxide layer.
 14. Asingle transistor DRAM cell provided on a semiconductor-on-insulator(SOI) substrate having a device layer disposed on a buried oxide layer,comprising: an n-type FET having source, drain and gate terminals, thedrain terminal being connected to a bit line and the source terminalbeing connected to a first storage capacitor, wherein the storagecapacitor comprises: a buried electrode disposed beneath the devicelayer; a capacitor dielectric overlying the buried electrode; and asecond electrode provided in the device layer overlying the capacitordielectric, the second electrode adapted to accumulate charge uponapplication of a bias voltage to the buried electrode.
 15. The DRAM cellof claim 14, further comprising a second storage capacitor having anupper electrode disposed above the device layer, a lower electrodedisposed in a single-crystal region of semiconductor material disposedbelow the device layer, the second storage capacitor being coupled tothe source terminal of the NFET.
 16. A method of fabricating a dynamictwo-phase shift register, comprising: forming a first field effecttransistor (FET) and a second FET, said first FET and said second FETeach having a channel region disposed in a common device layer of asemiconductor-on-insulator substrate, said first FET having a gateelectrode disposed beneath the common device layer and said second FEThaving a gate electrode disposed above the common device layer; andinterconnecting the gate electrode of the first FET to a first conductorfor providing a first clock signal; and interconnecting the gateelectrode of the second FET to a second conductor for providing a secondclock signal.
 17. An electronic chip containing a dynamic two-phaseshift register fabricated according to the method of claim 16, whereinthe gate electrodes of the first and second FETs transistor gates arevertically offset from each other.
 18. The electronic chip of claim 17,wherein the first and second FETs have non-overlapping channel regions.19. A method of fabricating a complementary metal oxide semiconductor(CMOS) circuit provided on a semiconductor-on-insulator (SOI) substrate,said method comprising: forming a plurality of field effect transistors(FETs), including a first FET and a second FET disposed in a commondevice layer, the first FET having a gate disposed on a first side ofthe common device layer the second FET having a gate disposed on ansecond side of the common device layer opposite the first side, thefirst and second FETs being interconnected by a common diffusion regionwithout requiring an intervening conductor.
 20. A chip including acomplementary metal oxide semiconductor (CMOS) circuit fabricatedaccording to the method of claim
 19. 21. The method of claim 19, furthercomprising: forming a conductor below said device layer, said conductorinterconnecting at least two of said FETs.
 22. The method of claim 21,wherein said conductor is formed at least partially enclosed by saidburied oxide layer.
 23. The method of claim 19, wherein said CMOScircuit includes at least one of a NOR circuit, and a NAND circuit.